ABSTRACTSYNTHESIS, PROPERTIES AND APPLICATIONS OF BIO-BASED MATERIALSByMadhusudhan SrinivasanBio-based feedstock have become very significant as they offer a value proposition in terms of carbon balance and also in terms of endowing biodegradability where needed. Thus a lot of attention is being given to the modification such feedstock for different applications. Soybean oil is one such feedstock. The oil is a triglyceride ester composed of different fatty acids, which are common to other plant oils. Thus soybean oil serves as a platform for plant oils, as modifications of this oil, can in theory be extended to cover other plant oils. Methyl oleate was used as a model fatty acid ester, to synthesize hydroxyesters with ethylene glycol via a two stage oxidative cleavage of the double bonds. Ozone was chosen as the oxidant due to its many advantages. The first stage involved oxidation of the double bond to aldehydes, ozonides and acetals, which were subsequently converted to hydroxyesters (hydroxy values of 220 - 270) in near quantitative yield by treatment with Oxone. This method could be extended to soybean oil to make "polyols" which could find applications in resin syntheses.Silylation was employed as another platform to functionalize soybean oil and fatty acid methyl esters with a reactive silane (vinyltrimethoxy silane). This simple modification produced materials that are cured by atmospheric moisture and are useful as coatings. The silylation was controlled by varying the grafting time, cure temperature and the concentration of the silane. Products with gel content as high as 90% could be achieved. The coating exhibited good adhesion to metal, glass, concrete and paper. Steel panels coated with these coatings exhibited good stability against corrosion in high humidity conditions and moderate stability against a salt spray.The silylation was also successfully utilized to improve the tensile strength of the blend of biodegradable polyester, poly (butylene adipate-co-terephthalate) with talc. A reactive extrusion process was employed to graft vinyl silanes on the polyester in short reaction times of 5 minutes. This improved the compatibility with the talc filler. This biodegradable polyester product was characterized by high tensile strength and moderate elongation. The modification method is simple is applicable to a variety of aliphatic biodegradable polyesters.Finally a rapid polymerization of 1, 4-dioxan-2-one in very short times was accomplished with titanium alkoxides as initiators. At low [monomer]/ [initiator] ratios (100:1), nearly all the alkoxide groups initiated polymerization. High conversions up to 90% were achieved even at high ratios (2400:1). The activation energy for polymerization for titanium tetraisopropoxide is the lowest reported (33.5 kJ/mol) for this monomer system.
Read